Titanium rod Standard ASTM B348 Material Ti6Al4V Gr.5

Titanium rods have high strength, low density, superior mechanical properties, and excellent corrosion resistance. It is widely used in: aerospace, ships, seawater desalination, seawater farming, offshore oil drilling, seawater pipelines, electric power industry, chemical petroleum industry, vacuum salt making, petrochemical, metallurgical industry, light industry, construction industry, sports equipment , Auto parts, bicycle parts, computers, cameras, watches, glasses, mobile phones, kitchen utensils, and handicrafts.

Product quality control

▲ Chemical analysis – to define element contents such as C, N, O, H, Fe, Al, V.
▲ Mechanical properties – tension test including tensile, yield, elongation, reduction of area
▲ Dimensional tolerance – diameter and length tolerance check
▲ Surface contamination – imperfections removed
▲ Nondestructive test – 100% NDT for inspecting inner cracks, pores, and other defections

Physical Properties:

Grade	Status	Tensile Strength		Yield Strength		Elongation	Area of Reduction
Grade	Status	Ksi	Mpa	Ksi	Mpa	%
GR1	Annealed	35	20	25	170	24	30
GR2		50	345	40	275	20	30
GR3		65	450	55	380	18	30
GR4		80	550	70	483	15	25
TI-6AL-4VELI		125	860	115	795	10	25
Ti6AL7Nb		130.5	900	116.8	800	10	25
Ti13Nb13Zr		ageing125 Solid 800 Not annealed 800	860 550 550	105 500 500	725 345 345	8 15 8	15 30 15

Precautions for use:

1 Avoid scratches, collisions, dust and oil.

2 The working pressure should not exceed the rated working pressure during use.

3 In normal use, there should be at least 3-5 minutes of low-pressure start-up time, and the relative pressure difference should be controlled below 0.5Mpa, and then the working pressure should be gradually adjusted to normal needs (the maximum pressure should not exceed 0.4Mpa).

4. After the product works for a certain period, it may be due to the clogging of the filter element, which may cause the pressure to increase and the flow rate to decrease, requiring backwashing or backwashing regeneration. The regeneration cycle depends on the rated pressure and flow.

Language

Language

Titanium bar

Round Titanium Alloy Rod AMS4928 TC11 Ti-6.5Al-3.5Mo-1.5Zr-0.3Si